Abstract
The effects of dilution of tetraethyl orthosilicate (TEOS) with ethanol on the shape and monodispersity of silica particles were investigated. The results indicated that the dilution of TEOS with ethanol can depress the formation of new nuclei and the aggregation or adhesion of particles and make the distillation of TEOS unnecessary to achieve monodispersed silica spheres. A seeded growth technique using continuous drop addition of TEOS diluted with 4× volume of ethanol was developed to improve monodispersity and spheric shape and increase the size of silica particles. The monodisperse silica particles (150 nm ± 5%−1.2 μm ± 1%) with fine spheric shape were successfully synthesized by the seeded growth technique. Using the homemade 280 nm ± 2.8% silica spheres, we prepared opals of high quality which showed periodically ordered packing and a photonic band-gap effect.
Similar content being viewed by others
References
G.R. Wiese and T.W. Healy, Trans. Faraday Soc. 66, 490 (1970).
J.Th.G. Overbeek, Adv. Colloid Interface Sci. 15, 251 (1982).
M.D. Sacks and T.Y. Tseng, J. Am. Ceram. Soc. 67, 526 (1984).
K.K. Unger and G. Jilge, J. Chromatogr. 359, 61 (1986).
R.D. Badly and W.T. Ford, J. Org. Chem. 54, 5347 (1989).
Y. Xia, B. Gates, Y. Ying, and Y. Lu . Adv. Mater. 12, 693 (2000).
G. Kolbe, The Complex Chemical Behavior of Silica, Dissertation, Jena, Germany (1956).
W. Stöber and A. Fink, J. Colloid Interface Sci. 26, 62 (1968).
A.K. Van Helden, J.W. Jansen, and A. Vrij, J. Colloid Interf. Sci. 81, 354 (1981).
G.H. Bogush, M.A. Tracy, and C.F. Zukoski, IV, J. Non-Cryst. Solids 104, 95 (1988).
E. Matijevic, Langmuir 10, 8 (1994).
P.G. Chen, P. Dong, B. Cheng, X. Li, and D. Zhang, Adv. Mater. 13, 437 (2001).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhang, J.H., Zhan, P., Wang, Z.L. et al. Preparation of monodisperse silica particles with controllable size and shape. Journal of Materials Research 18, 649–653 (2003). https://doi.org/10.1557/JMR.2003.0085
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2003.0085