Corrosion Inhibition of Carbon Steel in 1 M Hydrochloric Acid using Some Pyrazolo[3,4-d]Pyrimidnone Derivatives

  • Physicochemical Problems of Materials Protection
  • Published:
Protection of Metals and Physical Chemistry of Surfaces Aims and scope Submit manuscript

Abstract

The inhibiting effect of three compounds of pyrazolo[3,4-d] pyrimidnone derivatives toward the corrosion of carbon steel in 1.0M HCl solution was investigated using galvanostatic and potentiodynamic anodic polarization techniques. The rise of the concentration of the inhibitors and decreasing the temperature led to the greater of inhibition efficiency. The inhibiting action of these compounds was explicated on the footing of its adsorption on the carbon steel surface. The adsorption operation of these compounds was obeyed Langmuir isotherm. There is only one anodic peak during the anodic cyclic voltammogram This peak was elucidated due to the active dissolution of Fe as Fe2+. The percentage inhibition efficiency was computed from the values of peak current density.There is a good convention between the values of the percentage inhibition efficiency gained from the diverse techniques.These compounds inhibit the pitting corrosion of carbon steel by shifiting the pitting corrosion potential to more noble direction. The effect of elevation of temperature on the rate of corrosion in devoid of and containing these compounds was studied and some activated thermodynamic parameters were computed.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Sastri, V.S., Corrosion Inhibitors, New York: John Wiley and Sons, 1998.

    Google Scholar 

  2. Golestani, Gh., Shahidi, M., and Ghazanfari, D., Appl. Surf. Sci., 2014, vol. 308, p.347.

    Article  Google Scholar 

  3. Hosseini, M.G., Ehteshamzadeh, M., and Shahrabi, T., Electrochim. Acta, 2007, vol. 52, p. 3680.

    Article  Google Scholar 

  4. Abdallah, M., Zaafarany, I., Khairou, K., and Sobhi, M., Int. J. Electrochem. Soc., 2012, vol. 7, p. 1564.

    Google Scholar 

  5. Fouda, A.S., Abdallah, M., Al-Ashry, S.M., and Abdel-Fattah, A.A., Desalination, 2010, vol. 250, p.538.

    Article  Google Scholar 

  6. Mohamed Mustafa Ibrahim, Abdel Hameed, R.S., Abd-Alhakeem H. Abu-Nawwas, and Sawsan E. Mohamad, OCAIJ, 2014, vol. 10, p.271.

    Google Scholar 

  7. Abdallah, M. and Moustafa, M.E., Ann. Chim. (Rome, Italy), 2004, vol. 94, p.601.

    Article  Google Scholar 

  8. Fouda, A.S., Abdallah, M., and Medhat, M., Prot. Met. Phys. Chem. Surf., 2012, vol. 48, p.477.

    Article  Google Scholar 

  9. Abdallah, M., Al Jahdaly, B.A., and Al-Malyo, O.A., J. Electrochem. Sci., 2015, vol. 10, p. 2740.

    Google Scholar 

  10. Abdallah, M., AL Jahdaly, B.A., Sobhi, M., and Ali, A.I., Int. J. Electrochem. Sci., 2015, vol. 10, p. 4482.

    Google Scholar 

  11. Abdallah, M., Al Tass, H.M., AL Jahdaly, B.A., and Fouda, A.S., J. Mol. Liq., 2016, vol. 216, p.590.

    Article  Google Scholar 

  12. Sobhi, M., El-Sayed, R., and Abdallah, M., Chem. Eng. Commun., 2016, vol. 203, p.758.

    Google Scholar 

  13. Abdallah, M., Zaafarany, I.A., and AL Jahdaly, B.A., J. Mater. Environ. Sci., 2016, vol. 7, p. 1107.

    Google Scholar 

  14. Abdel Hameed, R.S., Hussin I. Al-Shafey, Ismail, E.A., et al., Int. J. Eng. Res. Appl., 2013, vol. 3, p. 1094.

    Google Scholar 

  15. AL Jahdaly, B.A., Althagafi, I.I., Abdallah, M., et al., J. Mater. Environ. Sci., 2016, vol. 7, p. 1798.

    Google Scholar 

  16. Abdallah, M., El-Etre, A.Y., and Soliman, M.G., Anti-Corros. Methods Mater., 2006, vol. 53, p.118.

    Article  Google Scholar 

  17. Abdallah, M., El-Dafrawy, A.M., Sobhi, M., et al., Int. J. Electrochem. Sci., 2014, vol. 9, p. 2186.

    Google Scholar 

  18. Abdel Hameed, R., Alshafey, H., Ali, F.A., et al., Int. J. Pharm. Sci. Rev. Res., 2014, vol. 27, p.146.

    Google Scholar 

  19. Abdel Hameed, R.S., Al Shafey, H.I., and Abu-Nawwas, A.H., Int. J. Electrochem. Sci., 2014, vol. 9, p. 6006.

    Google Scholar 

  20. Abdel hameed, R.S., Adv. Appl. Sci. Res., 2016, vol. 7, p.92.

    Google Scholar 

  21. Hanane, H., Douadi, T., Al-Noaimi, M., et al., Corros. Sci., 2014, vol. 88, p.234.

    Article  Google Scholar 

  22. Abdallah, M., Asghar, B., Zaafarany, I., and Sobhi, M., Prot. Met. Phys. Chem. Surf., 2013, vol. 49, p.485.

    Article  Google Scholar 

  23. Abdel Hameed, R.S., Shamroukh, A.H., and Abdallah, M., Jökull J., 2016, vol. 66, p.1.

    Google Scholar 

  24. El-Etre, A.Y., J. Colloid Interface Sci., 2007, vol. 314, p.578.

    Article  Google Scholar 

  25. Abdallah, M., Ann. Chim. (Rome, Italy), 1994, vol. 84, p.529.

    Google Scholar 

  26. AL Jahdaly, B.A., Althagafi, I.I., Abdallah, M., et al., J. Mater. Environ. Sci., 2016, vol. 7, p. 1798.

    Google Scholar 

  27. Putilova, J., Balezin, S., Bacannik, I.N., and Bishop, V.P., Metal Corrosion Inhibitors, Oxford: Pergamon, 1960, p. 1196.

    Google Scholar 

  28. Abdallah, M., Kamar, E.M., Salah Eid, and El-Etre, A.Y., J. Mol. Liq., 2016, vol. 220, p.755.

    Article  Google Scholar 

  29. Antropov, L.I., Theortical Electrochemistry, University Press of the Pacific, 2001.

    Google Scholar 

  30. Abdallah, M. and Megahed, H.E., Monatsh. Chem., 1995, vol. 126, p.519.

    Article  Google Scholar 

  31. Abdallah, M., Zaafarany, I., ElEtre, A.Y., and Kamar, A.M., Chem. Sci. Rev. Lett., 2014, vol. 3, p. 1348.

    Google Scholar 

  32. Abdallah, M., Al Karane, S.A., and Abdel Fattah, A.A., Chem. Eng. Commun., 2009, vol. 196, p. 1406.

    Article  Google Scholar 

  33. Abdallah, M., Al Karane, S.A., and Abdel, A.A., Chem. Eng. Commun., 2010, vol. 197, p. 1446.

    Article  Google Scholar 

  34. Jabir H. Al-Fahemia, Abdallah, M., Elshafie, A.M., J. Mol. Liq., 2016, vol. 222, p. 1157.

    Article  Google Scholar 

  35. Abdallah, M., Megahed, H.E., El-Naggar, M., et al., Bull. Electrochem., 2003, vol. 19, p.245.

    Google Scholar 

  36. Hanane Hamani, Tahar Douadi, Mousa Al-Noaimi, et al., Corros. Sci., 2014, vol. 88, p.234.

    Article  Google Scholar 

  37. Annand, R.R., Hurd, R.M., and Hackerman, N., J. Electrochem. Soc., 1965, vol. 112, p.144.

    Article  Google Scholar 

  38. Khamis, E., Corrosion, 1990, vol. 46, p.476.

    Article  Google Scholar 

  39. Stupnisek-Lisac, E. and Podbrscek, S., J. Appl. Electrochem., 1994, vol. 24, p. 779.

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Chemistry Department, Faculty of Science, Al-Azhar University, Cairo, 11884, Egypt

    R. S. Abdel Hameed

  2. Chemistry Departments, Faculty of Science, Hail University, Hail, 1560, Saudi Arabia

    R. S. Abdel Hameed

  3. Chemistry Department, Faculty of Applied Science, Umm Al-Qura, University, Makkah Al-Mukaramha, Saudi Arabia

    M. Abdallah

  4. Chemistry Department, Faculty of Science, Benha University, Benha, Egypt

    M. Abdallah

Authors
  1. R. S. Abdel Hameed
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. M. Abdallah
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to M. Abdallah.

Additional information

The article is published in the original.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Abdel Hameed, R.S., Abdallah, M. Corrosion Inhibition of Carbon Steel in 1 M Hydrochloric Acid using Some Pyrazolo[3,4-d]Pyrimidnone Derivatives. Prot Met Phys Chem Surf 54, 113–121 (2018). https://doi.org/10.1134/S2070205118010239

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1134/S2070205118010239

Keywords

Search

Navigation