The reaction of pyrrole and thiophene monomers with copper- or nickel-exchanged mordenite has been investigated using X-ray photoelectron (XPS) and photoacoustic infrared (PAIRS) spectroscopies. Because of the differing oxidising powers of the cations studied, polymerisation occurred only with copper-exchanged mordenite. PAIRS and XPS data indicated that both polypyrrole and polythiophene were partially oxidised when synthesised within the zeolite structure. IR spectra of polythiophene and polythiophene and polypyrrole showed intense bands typical of ring vibrations which could couple to the large dipole change induced by charges moving along the polythiophene chain. In addition it was noted that only vibrations typical of oxidised polymer structures were recorded, suggesting that the charge carrier was located within these segments. Furthermore, N 1s spectra contained a high binding energy peak at 402.5 eV which was attributed to a positively charged nitrogen species, in agreement with IR data. Significantly, C 1s spectra confirmed that molecular wires were formed within the confines of the zeolite lattice. Depth-profiling experiments suggested that polypyrrole was distributed throughout the entire zeolite host. By contrast, polythiophene may have been restricted to the uppermost zeolite channels owing to the ability of sulfur species to bond to Cu^I sites [produced by reduction of copper(II) ions during the polymerisation process], thus obstructing movement along the channels.