Compressive mechanical properties and microstructure of PVA–HA hydrogels for cartilage repair

Abstract

In this paper, hydroxyapatite (HA) was deposited on poly(vinyl alcohol) (PVA) molecular chains by an in situ synthetic method. Subsequently, combining cyclic freeze/thaw treatment, PVA–HA gel composites consisting of flexible PVA and rigid HA were prepared. The phase composition and structure of the PVA–HA hydrogels were investigated by XRD, IR and SEM methods, and their compressive mechanical properties were evaluated using mechanical test equipment. The results showed that PVA provides a flexible porous network skeleton to the hydrogel. The HA particles were distributed inside the pores and on the walls of the pores, strengthening the compressive properties of the PVA–HA hydrogel. Moreover, the increased PVA and HA contents could increase the compressive modulus and compressive strength of the hydrogel. The effect of the PVA content on the compressive mechanical properties of the hydrogel was predominant, especially at high strain rates. The maximum compressive strength of the PVA–HA hydrogel was 0.43 MPa, which remained even at a compression deformation rate up to 70%. The relationship between the compressive modulus and compression ratio tended to be an exponential function, same as the trend of the stress–strain curve. The results indicate that the prepared hydrogel is a viscoelastic material, which has potential for the application of articular cartilage repair.

Graphical abstract: Compressive mechanical properties and microstructure of PVA–HA hydrogels for cartilage repair

Article information

Article type
Paper
Submitted
25 Jan 2016
Accepted
29 Jan 2016
First published
11 Feb 2016

RSC Adv., 2016,6, 20166-20172

Compressive mechanical properties and microstructure of PVA–HA hydrogels for cartilage repair

W. Li, D. Wang, W. Yang and Y. Song, RSC Adv., 2016, 6, 20166 DOI: 10.1039/C6RA02166B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements