Unexpected shear dependence of pressure-induced γ-crystals in isotactic polypropylene†
Abstract
Flow and pressure frequently coexist in practical polymer processing operations, but their combined influence on the microstructure of polymer parts has received very limited attention in the academic community. In the current work, we utilized a home-made pressuring and shearing device with a reliable dynamic sealing design to study the formation and microstructure of γ-form isotactic polypropylene (iPP) obtained under the coexistence of flow and pressure. We observed a strong shear dependence of pressure-induced γ-form iPP. There are three regions depending on shear flow intensity, i.e., facilitation (<3.7 s−1), suppression (3.7–9.1 s−1) and inexistence (>9.1 s−1) regions of the γ-form. As the shear rate is below 3.7 s−1, the pressure-induced γ-form dominates and the shear flow slightly facilitates formation of γ-form. Unexpectedly, above 3.7 s−1, the shear flow is unfavorable for γ-form growth. Even under a pressure of 100 MP, a flow field with a shear rate above 9.1 s−1 could entirely suppress the γ-form. Moreover, we did not observe any trace of the β-form in the obtained iPP that is generally generated under shear flow alone. These interesting results have never been reported, which undoubtedly help manipulate the inner structure and thus enhance the performance of final iPP products.
Please wait while we load your content...