High strength films with gas-barrier fabricated from chitin solution dissolved at low temperature

Bo Duan; Chunyu Chang; Beibei Ding; Jie Cai; Min Xu; Shichao Feng; Jizhong Ren; Xiaowen Shi; Yumin Du; Lina Zhang

doi:10.1039/C2TA00068G

High strength films with gas-barrier fabricated from chitin solution dissolved at low temperature†

Bo Duan,^a Chunyu Chang,^a Beibei Ding,^a Jie Cai,*^a Min Xu,^b Shichao Feng,^c Jizhong Ren,^c Xiaowen Shi,^d Yumin Du^d and Lina Zhang*^a

Author affiliations

* Corresponding authors

^a Department of Chemistry, Wuhan University, Wuhan 430072, China
E-mail: lnzhang@public.wh.hb.cn, jiecaiwhu@hotmail.com
Fax: +86-27-68754067
Tel: +86-27-87219274

^b Department of Physics, East China Normal University, Shanghai 200062, China

^c Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, China

^d College of Resource and Environmental Sciences, Wuhan University, Wuhan, China

Abstract

The fabrication of pure chitin materials remains a challenge due to the difficult dissolution and regeneration of chitin. It has been a stumbling block for chitin research and utilization. In this work, chitin was dissolved completely in 11 wt% NaOH–4 wt% urea aqueous solution via the freezing/thawing method without derivatization, as supported by ¹³C NMR spectra. The pure regenerated chitin films with high strength were successfully prepared from the transparent chitin solution by coagulating with ethanol or 45 wt% dimethylacetamide (DMAc) aqueous solution. The influences of the interactions between the chitin solution and coagulants on the structure and properties of the chitin films were investigated by UV, FT-IR spectra, scanning electron microscopy, X-ray diffraction, nitrogen adsorption isotherms, thermo-gravimetric analysis and tensile testing, indicating the good coagulating condition. The dissolution and regeneration of chitin was confirmed to be an entirely physical processes. The chitin films possessed homogeneous structure, high optical transmittance (87% at 800 nm), moderate thermal stability, as well as excellent tensile strength (up to 111 MPa). Moreover, these chitin films had good gas barrier properties (0.003 barrer for oxygen permeability), indicating great potentials in the materials field. This work would open up a completely new avenue with green technology to investigate the most intransigent chitin.

Journal of Materials Chemistry A

High strength films with gas-barrier fabricated from chitin solution dissolved at low temperature†

Abstract

Supplementary files

Article information

Download Citation

Permissions

High strength films with gas-barrier fabricated from chitin solution dissolved at low temperature

Social activity

Search articles by author

Spotlight

Advertisements