Influence of titania on zirconia promoted Cu/SiO₂ catalysts for methanol synthesis from CO/H₂ and CO₂/H₂

Abstract

The effects of adding mixtures of titania and zirconia on the methanol synthesis activity and selectivity of Cu/SiO₂ were investigated. The synthesis of methanol from both CO/H₂ and CO₂/H₂ mixtures was examined at 0.65 MPa and temperatures between 448 and 573 K. For CO hydrogenation, the addition of ZrO₂ alone increased the methanol synthesis activity of Cu/SiO₂ by up to three-fold. Substitution of a portion of the ZrO₂ by TiO₂ decreased the methanol synthesis activity of the catalyst relative to that observed when only ZrO₂ is added. ZrO₂ addition also enhanced the methane synthesis activity by as much as seven fold. In the case of CO₂ hydrogenation, the maximum methanol synthesis activity is achieved when a 50/50 wt% mixture of ZrO₂ and TiO₂ is added to Cu/SiO₂. Neither the presence of the oxide additive nor its composition had any effect on the activity of the reverse water–gas-shift reaction, which suggests that this reaction proceeds only on Cu. The observed effects of ZrO₂ and TiO₂ on the catalytic activity of methanol synthesis from CO and CO₂, and methane synthesis from CO, are interpreted in terms of the strength and concentration of acidic and basic groups on the surface of the dispersed oxide.