On the plastic deformation of the amorphous component in semicrystalline polymers
Abstract
The molecular orientation of the amorphous component of semicrystalline high-density polyethylene (HDPE) induced by plane strain compression was studied by wide-angle X-ray scattering measurements utilizing the pole figure technique and separation of the scattering produced by the crystalline and amorphous components. It was found that the oriented amorphous component produced by large strain plastic deformation consists of domains of extended chain segments, closely packed in a two-dimensional pseudo-hexagonal aggregation, which are separated by less ordered regions. The deformation leads to the formation of a texture of the amorphous component which is common to the whole sample. In this texture, the direction of the chains coincides with the direction of flow, and one of the (100) pseudo-planes of the pseudo-hexagonal structure in every domain is perpendicular to the loading direction. It was suggested that the most important deformation mechanisms in the ordered amorphous component were the glide of the chain segments along their axes and the slip of the pseudo-planes of the ordered chains in the direction perpendicular to the chain axis, with resembling the crystallographic slip processes. Such a specific deformation of the amorphous layers most probably resulted from the strong constraint imposed by the slip deformation in the crystalline component to which the amorphous component is intimately connected.
References (25)
- B.J. Lee et al.
Polymer
(1993) - R.G. Kirste et al.
Polymer
(1975) - G.R. Mitchell et al.
Polymer
(1982) - A.G. Gibson et al.
Polym.
(1978) - H. Schönherr et al.
Polymer
(1995) - P.B. Bowden et al.
J. Mater. Sci.
(1974) - J.M. Haudin
- L. Lin et al.
J. Mater. Sci.
(1994) - A. Keller et al.
J. Mater. Sci.
(1971) - D.P. Pope et al.
J. Polym. Sci. Polym. Phys. Edn
(1975)
Macromolecules
Macromolecules
Cited by (114)
Time courses of strains that induce necking and fracturing in high-density polyethylene
2023, Polymer TestingHigh-density polyethylene is widely used in pressure pipe applications, but its necking and pre-cut effects are still poorly understood. Herein, we analyze the spatial distributions of the time courses of strains to highlight the strain field evolution to necking and the effect of pre-cutting on the strain field evolution in a high-density polyethylene material deformed under tension. Digital image correlation was used to measure the strain fields on two perpendicular surfaces of a specimen. Necking and its propagation in the tension direction dominate the failure behavior of an intact specimen. However, in the pre-cut specimen, crack propagation prevents neck propagation in the tension direction. Energy release outside the crack zone is observed as a decrease in strain at approximately the failure time. This leads to a macroscopic stress-strain curve that deviates from that of the intact specimen. These findings provide novel insights that are significant in the theoretical modelling and simulations of advanced polymeric materials and structures.
Intrahelical empty channels of nanoporous-crystalline α and β forms of PPO
2022, European Polymer JournalA linear dichroism study of vibrational peaks of amorphous and semi-crystalline axially stretched poly(2,6-dimethyl-1,4-phenylene)oxide (PPO) films shows an unusual behaviour of co-crystalline and nanoporous-crystalline (α and β form) phases. In fact, signs of dichroism for all vibrational peaks of α and β phases are opposite with respect to those observed for amorphous phases. This behaviour indicates the occurrence in PPO α and β forms of large polymer helices, whose thermodynamic stability can be rationalized by placement of guest molecules in intrahelical channels. A large diameter helix, with chain periodicity of 1.06 nm, is compatible with layer-line position in WAXD patterns of axially stretched α form films. The occurrence for both α and β NC forms of PPO of intrahelical empty channels, can rationalize the very high guest diffusivity of semi-crystalline PPO films, which becomes particularly high when crystalline helical axes are preferentially perpendicular to the film plane.
A nanoscale study of size scale, strain rate, temperature, and stress state effects on damage and fracture of polyethylene
2021, Mechanics of MaterialsThe mechanical properties and damage behavior of amorphous polyethylene are investigated using Molecular Dynamics (MD) simulations. The influence of time, temperature, size scale, and stress state are extensively studied to gather insights into the complex nature of glassy polymers and the related damage process of void formation during dynamic loading conditions. The Modified Embedded Atom Method (MEAM) is employed to model interatomic interactions, balancing computational efficiency with a superior description of free surfaces and void formation to provide a detailed analysis of the progression of damage in the form of nucleation, growth, and coalescence of voids. The MD simulations capture the evolution of the number and size of voids and are shown to correlate to specific regimes of the stress-strain response. Particular attention is given to the quantification of void coalescence and the influence coalescence has on the growth and nucleation rates of voids. A nanoscale parameter, the critical Inter-void Ligament Distance (ILD), is defined for the initiation of void coalescence, and is found to be about 0.75 void diameters resulting in the enhancement of void growth and the restriction of void nucleation once the critical ILD is achieved. This study provides important insight into the damage progression of glassy polymers that cannot be defined through current experimental techniques.
Nanocavitation mechanisms in deformed High Density PolyEthylene (HDPE) using synchrotron radiation NanoTomography
2021, PolymerThe nanocavitation distribution in deformed High Density PolyEthylene (HDPE) was investigated. A flat notched sample of HDPE, deformed under steady crosshead speed up to the end of the stress softening, was observed by classical synchrotron parallel beam microtomography and magnified holotomography with a true spatial resolution of 0.7 μm and 0.05 μm, respectively. Image processing, 3D image segmentation and 2D-Fast Fourier Transform, was shown to lead to quantification of void volume fraction and void size distributions. Nanocavitation morphology and distribution in HDPE reveal to be similar to cavitation mechanisms in other semi-crystalline polymers, but at a different scale. While a slight decrease of the void diameter was seen, from the end of the neck shoulder to the extended neck region, a significant increment of the height was evidenced. Furthermore, the results provide compelling evidence of morphology transition of cavities within the test sample from an oblate to a prolate geometry.
Creep behavior and modeling of high-density polyethylene (HDPE)
2021, Polymer TestingCreep behavior of high-density polyethylene (HDPE) was investigated. HDPE has many engineering applications in different industries such as piping systems, cable and wiring, automotive parts, storage containers, and biomedical implants. The temperatures chosen were 23, 53, and 82 °C based on the service temperature range for application in design of automotive fuel tanks. Creep strength decreased and creep strain as well as creep strain rate increased by increasing temperature. The Larson-Miller parameter widely used for metallic materials was able to correlate time to rupture, stress, and temperature data of HDPE. The Monkman-Grant relation was successfully used to correlate minimum creep rate and time to rupture. The Findley power law and time-stress superposition principle (TSS) were used to represent nonlinear viscoelastic creep curves. Some longer-term creep tests were also conducted at room temperature to evaluate the accuracy of extrapolation of the short-term creep test results to longer creep life predictions. The models used based on the data presented can be used in the design of parts and components made of HDPE where creep failure may be a concern.
Anomalously enhanced toughness of poly (lactic acid) nanocomposites by core-shell particles with high thickness soft shell
2020, Composites Part A: Applied Science and ManufacturingThe anomalous improvement in ductility and toughness of biodegradable poly (lactic acid) (PLA) was achieved by incorporating the silica-g-poly(caprolactone-co-lactide) (SiO2-PCLLA) core-shell nanoparticle with high thickness rubber shell. The variation of mechanical properties and toughening mechanism of nanocomposites with rubber shell thickness were investigated via tensile tests and surface morphology observation, X-ray scattering (SAXS) and diffraction (WAXD). The experimental results showed that the core-shell nanoparticle with high thickness rubber shell of 25 nm extremely remarkably improved the ductility and toughness of nanocomposite, about 34 times higher than those of neat PLA, particularly nearly without reducing its strength. This considerable increment of toughness is attributed to that the cavitation occurred in thick rubber shell can induce the intense plastic flow of matrix, forming the fibrillated structure like ‘bamboo joint’. In addition, it was found that the toughening of PLA is not only related to the rubber shell thickness, but also to the added nanofiller content.