Rheological and Mechanical Properties, Acid Resistance and Water Penetrability of Lightweight Self-Compacting Concrete Containing Nano-SiO2, Nano-TiO2 and Nano-Al2O3

  • Research Paper
  • Published:
Iranian Journal of Science and Technology, Transactions of Civil Engineering Aims and scope Submit manuscript

Abstract

This paper presents rheological and strength properties, acid resistance and water penetrability of lightweight self-compacting concrete (LWSCC) containing nano-SiO2 (NSi), nano-TiO2 (NTi) and nano-Al2O3 (NAl) as a partial substitute of cement. For this aim, one part of cement was replaced by 2 and 4 wt% of NSi, 2 and 4 wt% of NTi and 1 and 2 wt% of NAl. In addition, the rheological properties of LWSCCs were quantitatively evaluated by slump flow diameter, V-funnel flow time, J-ring, U-box and L-box height ratio. Then, the mechanical properties of LWSCCs were evaluated by compressive and splitting tensile strength tests at 3, 7 and 28 days of curing, while the water penetrability of LWSCC samples was evaluated by the water permeability test. The specimens were exposed to 5% sulfuric acid solution up to the age of 70 days, and the corrosion was identified in terms of mass loss and retained compressive strength. It was also found that all the LWSCCs containing nanoparticles show a good behavior in terms of deformability, passing ability and resistance to segregation. Results indicated that the incorporation of nanoparticles can improve the compressive strength, acid resistance and water penetrability of LWSCCs. In addition, the SEM tests revealed that the microstructure of LWSCCs with nanoparticles was more homogenous and compact than that of the control samples.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18

Similar content being viewed by others

References

Download references

Funding

This study has not been funded.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Yousef Askari Dolatabad.

Ethics declarations

Conflict of interest

The authors declare that they have no conflict of interest.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Askari Dolatabad, Y., Kamgar, R. & Gouhari Nezad, I. Rheological and Mechanical Properties, Acid Resistance and Water Penetrability of Lightweight Self-Compacting Concrete Containing Nano-SiO2, Nano-TiO2 and Nano-Al2O3. Iran J Sci Technol Trans Civ Eng 44 (Suppl 1), 603–618 (2020). https://doi.org/10.1007/s40996-019-00328-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s40996-019-00328-1

Keywords

Navigation