Abstract
Preliminary extraction research was carried out to develop a suitable dilute alkali pretreatment–sulfuric acid leaching process for uranium recovery from tailings containing 80 ppm uranium. The effects of alkali concentration, liquid-to-solid ratio, stirring speed and leaching time on uranium content in the leaching residues were investigated. The results showed that the leaching efficiency of dilute alkali pretreatment–sulfuric acid leaching is superior to direct acid leaching. Only 13 ppm and 7.5 ppm of uranium remained in tailings by using NaOH and Na2CO3, respectively, with an alkali concentration of 10 g/L, a liquid-to-solid ratio of 20, and an agitation of 400 rpm for 2 h. In addition, uranium liberation was significantly promoted by forming pores during the leaching process. This technology has advantages of low energy consumption, high leaching efficiency and less impurity production compared to traditional direct acid leaching.
Similar content being viewed by others
References
S. Abhilash, K.D. Singh, V. Mehta, K.B.D. Pandey, and V.M. Pandey, Hydrometallurgy 95, 70 (2009).
W.L. Xing, A.J. Wang, Q. Yan, and S. Chen, Ann. Nucl. Energy 110, 1156 (2017).
J.Q. Pan, C. Zhang, Y.Z. Sun, Z.H. Wang, and Y.S. Yang, Electrochem. Commun. 19, 70 (2012).
K. Inoue and S. Alam, JOM 65, 1341 (2013).
M. Omran, T. Fabritius, A.M. Elmahdy, N.A. Abdel-Khalek, and S. Gornostayev, Sep. Purif. Technol. 156, 724 (2015).
C.R. Yang, W.Q. Qin, S.S. Lai, J. Wang, Y.S. Zhang, F. Jiao, L.Y. Ren, T. Zhuang, and Z.Y. Chang, Hydrometallurgy 106, 32 (2011).
S.J. Zhen, Z.Q. Yan, Y.S. Zhang, J. Wang, M. Campbell, and W.Q. Qin, Hydrometallurgy 96, 337 (2009).
Y. Meguro, Z. Yoshida, O. Tomioka, Y. Enokida, and I. Yamamoto, J. Supercrit. Fluids 31, 141 (2004).
N. Dhawan, M.S. Safarzadeh, J.D. Miller, S. Moats, and R.K. Rajamani, Miner. Eng. 41, 53 (2013).
P.K. Kalsi, B.S. Tomar, K.L. Ramakumar, and V. Venugopal, J. Radioanal. Nucl. Chem. 293, 863 (2012).
J. Yuan, J. Xiao, F. Li, B. Wang, Z. Yao, B. Yu, and L. Zhang, Ultrason. Sonochem. 41, 608 (2018).
Y.S. Ladola, S. Chowdhury, S.B. Roy, and A.B. Pandit, Desalin. Water Treat. 52, 407 (2014).
B. Joseph, K.A. Venkatesan, K. Nagarajan, T.G. Srinivasan, and P.R. Vasudeva Rao, J. Radioanal. Nucl. Chem. 287, 167 (2011).
B.Q. Lu, M. Li, X.W. Zhang, C.M. Huang, X.Y. Wu, and Q. Fang, J. Hazard. Mater. 343, 255 (2018).
Y.F. Zhao and J. Chen, J. Nucl. Mater. 373, 53 (2008).
V. Madakkaruppan, A. Pius, S.T.N. Giri, and C. Sarbajna, J. Hazard. Mater. 313, 9 (2016).
N. Lippiatt and F. Bourgeois, Miner. Eng. 31, 71 (2012).
M.J. Lottering, L. Lorenzen, N.S. Phala, J.T. Smit, and G.A. Schalkwyk, Miner. Eng. 21, 16 (2008).
F.K. Crundwel, Hydrometallurgy 149, 11 (2014).
C.R. Edwards and A.J. Oliver, JOM 52, 12 (2000).
D. Lunt, P. Boshoff, M. Boylett, and Z. El-Ansary, J. South. Afr. Inst. Min. Metall. 107, 419 (2017).
B.J. Youlton and J.A. Kinnaird, Miner. Eng. 52, 62 (2013).
G.M. Ritcey and A.W. Ashbrook, Solvent Extraction: Principles and Applications to Process Metallurgy (Amsterdam: Elsevier, 1984).
B. Zhang, M. Li, X.W. Zhang, and J. Huang, JOM 68, 1990 (2016).
E.N. Malenga, A.F. Mulaba-Bafubiandi, and W. Nheta, Hydrometallurgy 155, 65 (2015).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Grant Nos. 51404141, 51874180), China Postdoctoral Science Foundation (Grant No. 2015M572255), natural science foundation of Hunan Province (Grant No.2018JJ3437) and the double first class construct program of USC (2017SYL05).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Huang, C., Li, M., Zhang, X. et al. Uranium Extraction from Tailings by Dilute Alkali Pretreatment–Sulfuric Acid Leaching Technology. JOM 70, 2746–2752 (2018). https://doi.org/10.1007/s11837-018-3127-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-018-3127-2