Abstract
The precursor of plate-like Li3PS4 solid electrolyte (75Li2S▪25P2S5, SE (LS)), about 3 μm in length, 500 nm in width, and 100–200 nm in thickness, was successfully prepared from Li2S and P2S5 using ethyl propionate (EP) as a synthetic medium via liquid-phase shaking. Upon evacuating at 170 °C, the precursor decomposed to SE (LS), which exhibited ionic conductivity of about 2.0 × 10−4 Scm−1 at room temperature. SEM observation revealed that the SE (LS) thus obtained had plate-like morphology with dimension of 3 μm in length, 500 nm in width, and 100–200 nm in thickness. Owing to the nanosized SE (LS), an all-solid-state half-cell using composite anode consisting of 90 wt% LiNi1/3Mn1/3Co1/3O2 (NMC) and 10 wt% SE (LS) delivered a high capacity up to 130 mAhg−1(NMC) at the first discharge.
Similar content being viewed by others
References
Tarascon JM, Armand M (2001) Nature 414:359–367
Tarascon JM (2010) Philos T Roy Soc A 368:3227–3241
Sakuda A, Hayashi A, Tatsumisago M (2013) Scientific Rep 3:2261
C. Cao, Z.-B. Li, X.-L. Wang, X.-B. Zhao, W.-Q. Han (2014) Fron. Energy Res., 2, article 25.
Tarascon JM (2002) Actualité Chimique 251:130–137
Sakuda A, Takeuchi T, Kobayashi H (2016) Solid State Ionics 285:112–117
Teragawa S, Aso K, Tadanaga K, Hayashi A, Tatsumisago M (2014) J Mat Chem A 2:5095–5099
Yubuchi S, Teragawa S, Aso K, Tadanaga K, Hayashi A, Tatsumisago M (2015) J Power Sources 293:941–945
Kim J, Eom M, Noh S, Shin D (2013) J Power Sources 244:476–481
Phuc NHH, Totani M, Morikawa K, Muto H, Matsuda A (2016) Solid State Ionics 288:240–243
ICH Guidance for Industry, Q3C Tables and List. http://www.fda.gov/Drugs/GuidanceComplianceRegulatoryInformation/Guidances/default.htm
Phuc NHH, Morikawa K, Totani M, Muto H, Matsuda A (2016) Solid State Ionics 285:2–5
Dutta B, Tanaka T, Banerjee A, Chowdhury J (2013) J Phys Chem A 117:4838–4850
Liu Z, Fu W, Payzant EA, Yu X, Wu Z, Dudney NJ, Kiggans J, Hong K, Rondinone AJ, Liang C (2013) J Am Chem Soc 135:975–978
Hayashi A, Hama S, Morimoto H, Tatsumisago M, Minami T (2001) J Am Ceram Soc 84:477–479
Teragawa S, Aso K, Tadanaga K, Hayashi A, Tatsumisago M (2014) JPower Sources 248:939–942
Tachez M, Malugani JP, Mercier R, Robert G (1984) Solid State Ionics 14:181–185
James DW, Mayes RE (1984) J Phys Chem 88:637–642
Kim Y-S, Jeong S-K (2015) J Spec 2015:1–5
Hayashi A, Hama S, Minami T, Tatsumisago M (2003) Electrochem Commun 5:111–114
Sata N, Elberman K, Eberl K, Maier J (2000) Nature 408:946–949
Homma K, Yonemura M, Kobayashi T, Nagao M, Hirayama M, Kanno R (2011) Solid State Ionics 182:53–58
Sakuda A, Hayashi A, Tatsumisago M (2010) Chem Mater 22:949–956
Acknowledgements
This study was supported by the Advanced Low Carbon Technology Specially Promoted Research for Innovative Next Generation Batteries (JST-ALCA-SPRING) program of the Japan Science and Technology Agency. The authors thank Prof. Tatsumisago (Osaka Prefecture University), Prof. Hayashi (Osaka Prefecture University), and Dr. Sakuda (National Institute of Advanced Industrial Science and Technology, AIST) for their assistance and useful discussions. The authors also gratefully acknowledge Dr. Tsukasaki and Prof. Mori of Osaka Prefecture University, Dr. Kobayashi and Dr. Takahashi of Osaka Municipal Technical Research Institute for their assistance in TEM and SEM observations.
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Phuc, N.H.H., Morikawa, K., Mitsuhiro, T. et al. Synthesis of plate-like Li3PS4 solid electrolyte via liquid-phase shaking for all-solid-state lithium batteries. Ionics 23, 2061–2067 (2017). https://doi.org/10.1007/s11581-017-2035-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11581-017-2035-8