The influences of shearing conducted by a Brabender rheometer on phase morphology, thermal and rheological behavior of a commercial impact polypropylene copolymer (IPC) were studied. The crystallization and melting traces show that short-time annealing at 210°C is unable to completely erase the influence of shearing on the samples. When the samples which were treated at a rotation speed of 80 r/min crystallize at a cooling rate of 10 K/min, their T cs and corresponding T ms obviously rise with the increase of shearing time. Furthermore, the POM results reveal that the shearing can lead to the formation of shish-kebab and the shish-kebab amount is proportional to shearing time. The rheological measurement results show that the treated samples exhibit different G′∼ω dependences. The ‘second plateau’ appears when the sample is treated at a rotation speed of 60 r/min or 80 r/min for 10 min, and linear G′∼ω dependence is observed at other rotation speeds. In addition, it is found that the appearance of the ‘second plateau’ depends on the shearing time when the rotation speed is fixed. According to SEM observations, it is proposed that the ‘second plateau’ of IPC samples should be ascribed to the aggregation of dispersion particles.
Similar content being viewed by others
References
Jang, B.Z., Uhlmann, D.R. and Sande, J.B.V., J. Appl. Polym. Sci., 1985, 30: 2485
Liang, J.Z. and Li, R.K.Y., J. Appl. Polym. Sci., 2000, 77: 409
Tam, W.Y., Cheung, T. and Li, R. K.Y., Polym. Test., 1996, 10: 363
Chen, R.F., Shangguan, Y.G., Zhang, C.H., Chen, F. and Zheng, Q., Polymer, 2011, 52: 2956
Yokoyama, Y. and Ricco, T., Polymer, 1998, 39: 3675
Debling, J.A. and Ray, W.H., J. Appl. Polym. Sci., 2001, 81: 3085
Prasetya, A., Liu, L., Litster, J., Watanabe, F., Mitsutani, K. and Ko, G.H., Chem. Eng. Sci., 1999, 54: 3263
Zacca, J.J., Debling, J.A. and Ray, W.H., Chem. Eng. Sci., 1997, 52: 1941
Dong, Q., Wang, X.F., Fu, Z.S., Xu, J.T. and Fan, Z.Q., Polymer, 2007, 48: 5905
Zhang, C.H., Shangguan, Y.G., Chen, R.F., Wu, Y.Z., Chen, F., Zheng, Q. and Hu, G.H., Polymer, 2010, 51: 4969
Chen, Y., Chen, Y., Chen, W. and Yang, D.C., Eur. Polym. J., 2007, 43: 2999
Cai, H.J., Luo, X.L., Ma, D.Z., Wang, J.M. and Tan, H.S., J. Appl. Polym. Sci., 1999, 71: 93
Fan, Z.Q., Zhang, Y.Q., Xu, J.T., Wang, H.T. and Feng, L.X., Polymer, 2001, 42: 5559
Song, S.J., Wu, P.Y., Feng, J.C., Ye, M.X. and Yang, Y.L., Polymer, 2009, 50: 286
Hanafy, G., Madbouly, S.A., Ougizawa, T. and Inoue, T., Polymer, 2005, 46: 705
Tong, W., Huang, Y.J., Liu, C.L., Chen, X.L., Yang, Q. and Li, G.X., Colloid Polym. Sci., 2010, 288: 753
Vananroye, A., Puyvelde, P.V. and Moldenaers, P., Langmuir, 2006, 22: 2273
Keestra, B.J., Goossens, J.G.P. and Anderson, P.D., Chem. Eng. Sci., 2011, 66: 4960
Wang, Y., Meng, K., Hong, S., Xie, X.M., Zhang, C.G. and Han, Charles C., Polymer, 2009, 50: 636
Boiko, Y.M., Colloid Polym. Sci., 2011, 289: 971
Kitade, S., Ichikawa, A., Imura, N., Takahashi, Y. and Noda, I., J. Rheo., 1997, 41: 1039
Luo, K.F. and Yang, Y.L., Macromol. Theory Simul., 2002, 11: 429
Chen, Q., Yu, W. and Zhou, C.X., J. Polym. Sci. Polym. Phys., 2008, 46: 431
Xie, Y.L., Shangguan, Y.G. and Zheng, Q., Acta Polymerica Sinica (in Chinese), 2008, (1): 93
Ferry, J.D., “Viscoelastic properties of polymers”, John Wiley & Sons, New York, 1980
Du, M., Gong, J.H. and Zheng, Q., Polymer, 2004, 45: 6725
Wu, G., Song, Y.H., Zheng, Q., Du, M. and Zhang, P.J., J. Appl. Polym. Sci., 2003, 88: 2160
Fu, Q., “Injection-molded polyolefin: morphorlogical controlling and properties”, Science Press, Beijing, 2007
Tan, H.S., Xie, K., Liu, W. H., Hou, B., Shangguan, Y.G. and Zheng, Q., Acta Polymerica Sinica (in Chinese), 2006, (9): 1106
Song, S.J., Feng, J.C., Wu, P.Y. and Yang, Y.L., Macromolecules, 2009, 42: 7067
Author information
Authors and Affiliations
Corresponding authors
Additional information
This work was financially supported by the National Natural Science Foundation of China (No. 51173157), National Basic Research Program of China (No. 2005CB623800) and Natural Science Foundation of Zhejiang Province (No. Y4100314).
Rights and permissions
About this article
Cite this article
Wu, Y., Liang, Xy., Chen, Rf. et al. Influence of shearing on impact polypropylene copolymer: Phase morphology, thermal and rheological behavior. Chin J Polym Sci 30, 470–477 (2012). https://doi.org/10.1007/s10118-012-1145-z
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10118-012-1145-z