Abstract
Slow crack growth in two forms of polymethylmethacrylate (PMMA) has been studied from a fracture mechanics viewpoint. It has been found that in Perspex acrylic sheet and surgical Simplex acrylic bone cement the crack velocity, V, for each material depends upon the intensification of stress at the tip of the crack. Experimental measurements have been made of V as a function of the stress intensity factor, K I, at the crack tip, and a derived V(K) relationship has been used to predict the times-to-failure of components made from Perspex and Simplex bone cement. Direct measurements of times-to-failure for Perspex are entirely consistent with the predicted values.
Similar content being viewed by others
References
R. P. Kambour, J. Polymer Sci. Macromol. Rev. 7 (1973) 1.
H. G. Nelson, A. S.Tetelman and D. P. Williams, Proceedings of the International Conference on Corrosion Fatigue, Storrs, Connecticut, June (1971).
S. M. Wiederhorn, J. Amer. Ceram. Soc. 50 (1967) 407.
A. G. Evans, J. Mater. Sci. 7 (1972) 1137.
J. G. Williams and G. P. Marshall, Proc. Roy. Soc., to be published.
G. P. Marshall, L. H. Coutts and J. G. Williams, J. Mater. Sci. 9 (1974) 1409.
A. G. Evans, Int. J. Fracture 9 (1973) 267.
H. R. Brown and I. Ward, Polymer 14 (1973) 469.
P. W. R. Beaumont and R. J. Young, J. Biomed. Mats. Res., to be published.
S. N. Zhurkov, Int. J. Fracture Mechs. 1 (1965) 311.
F. Bueche, “Physical Properties of Polymers”, (Interscience, New York, 1962), Ch. 11.
J. P. Berry, in “Fracture Processes in Polymeric Solids”, edited by B. Rosen (Interscience, New York, 1964) Ch. II.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Beaumont, P.W.R., Young, R.J. Failure of brittle polymers by slow crack growth. J Mater Sci 10, 1334–1342 (1975). https://doi.org/10.1007/BF00540823
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00540823