Abstract
Laser scanning confocal microscopy (LSCM) has been used to characterize the changes in film thickness and local surface morphology of polymer coatings during the UV degradation process. With the noninvasive feature of LSCM, one can obtain thickness information directly and nondestructively at various exposure times without destroying the specimens or deriving the thickness values from IR measurement by assuming uniform film ablation. Two acrylic polymer coatings were chosen for the study, and the physical and chemical changes of the two systems at various exposure times were measured and analyzed. Those measurable physical changes caused by UV exposure include film ablation, formation of pits and other surface defects, and increases in surface roughness. It was found in both coatings that changes in measured film thickness by LSCM were not correlated linearly to the predicted thickness loss using the changes in the CH band obtained by the Fourier Transform Infrared (FTIR) spectroscopy measurements in the later degradation stages. This result suggested it was not a uniform film ablation process during the UV degradation. At later stages, where surface deformation became severe, surface roughness and profile information using LSCM were also proven to be useful for analyzing the surface degradation process
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Bauer, D.R. and Martin, J.W. (Eds.), Service Life Prediction of Organic Coatings: A Systems Approach, ACS Symposium Series, 722, Oxford University Press, 1999.
Wernst⇘hl, K.M., “Service Life Prediction of Automotive Coatings, Correlating Infrared Measurements and Gloss Retention,” Polym. Degrad. Stab., 54, 57 (1996).
Gerlock, J.L., Smith, C.A., Cooper, V.A., Dubiber, T.G., and Weber, W.H., “On the Use of Fourier Transform Infrared Spectroscopy and Ultraviolet Spectroscopy to Assess the Weathering Performance of isolated Clearcoats from Different Chemical Families,” Polym. Degrad. Stab., 62, 255 (1998).
Martin, J., Nguyen, T., Byrd, E., Dickens, B., and Embree, N., “Relating Laboratory and Outdoor Exposures of Coatings: I Cumulative Damage Model and Laboratory Experiment Apparatus,” Polym. Degrad. Stab., 75, 193 (2002).
Nguyen, T., Martin, J., Byrd, E., and Embree, N, “Relating Laboratory and Outdoor Exposures of Coatings: II. Effects of Relative Humidity on Photodegradation of Acrylic Melamine,” Journal of Coatings Technology, 74, No. 932, 31 (2002).
Croll, S.G. and Skaja, A.D., “Quantitative Spectroscopy to Determine the Effects of Photodegradation on a Model Polyester-Urethane Coatings,” Journal of Coatings Technology, 75, No. 945, 85 (2003).
Smith, C.A., Gerlock, J.L., Kucherov, A.V., Misovski, T., Seubert, C.M. Carter, R.O. III, and Nichols, M.E. “Evaluation of Accelerated Weathering Tests for Automotive Clears Using Transmission Fourier Transform Infrared Spectroscopy”, Proc. of the FSCT 80th Annual Meeting, Oct. 30-Nov 1, New Orleans, LA (2002).
Gerlock, J.L., Peters, C.A., Kucherov, A.V., Misovski, T., Seubert, C.M., Carter, R.O. III, and Nichols, M.E., “Testing Accelerated Weathering Tests for Appropriate Weathering Chemistry: Ozone Filtered Xenon Arc,” Journal of Coatings Technology, 75, No. 936, 35 (2003).
Osterhold, M. and Glöckner, P., “Influence of Weathering on Physical Properties of Clearcoats,” Prog. Org. Coat., 41, 177 (2001).
Johnson, M.A., and Cote, P.J., “Detrended Fluctuation Analysis of UV Degradation in a Polyurethane Coatings,” Journal of Coatings Technology, 75, No. 941, 51 (2003).
VanLandingham, M.R., Nguyen, T., Byrd, W.E., and Martin, J.W., “On the Use of the Atomic Force Microscope to Monitor Physical Degradation of Polymeric Coating Surfaces,” Journal of Coatings Technology, 73, No. 923, 43 (2001).
McKnight, M.E., Marx, E., Nadal, M., Vorburger, T.V., Barnes, P.Y., and Galler, M.A., “Measurements and Predictions of Light Scattering by Clear Epoxy Coatings,” Applied Optics, 40, No. 13, 2159 (2001).
Sung, L., Nadal, M.E., McKnight, M.E., Marx, E., and Laurenti, B., “Optical Reflectance of Metallic Coatings: Effect of Aluminum Flake Orientation,” Journal Coatings Technology, 74, No. 932, 55 (2002).
Hunt, F.Y., Marx, E., Meyer, G.W., Vorburger, T.V., Walker, P.A., and Westlund, H.B., “A First Step Towards Photorealistic Rendering of Coated Surfaces and Computer Based Standards of Appearance,” in Service Life Prediction: Methodology and Metrologies, Martin, J.W. and Bauer, D.R., (Eds.), ACS Symposium Series 805, 437, Oxford University Press, 2002.
Corle, T.R. and Kino, G.S., Confocal Scanning Optical Microscopy and Related Imaging Systems, pp. 37–39, Academic Press, 1996.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sung, LP., Jasmin, J., Gu, X. et al. Use of laser scanning confocal microscopy for characterizing changes in film thickness and local surface morphology of UV-exposed polymer coatings. J Coat. Technol. Res. 1, 267–276 (2004). https://doi.org/10.1007/s11998-004-0029-8
Issue Date:
DOI: https://doi.org/10.1007/s11998-004-0029-8