Transient liquid-phase infiltration (TLI) is a new method for densifying a powder-metal skeleton that produces a final part of homogeneous composition without significant dimensional change, offering advantages over traditional infiltration and full-density sintering. Fabrication of direct metal parts with complex geometry is possible using TLI in conjunction with solid freeform fabrication (SFF) processes such as three-dimensional printing, which produce net-shape powder-metal skeletons directly from computer-aided design models. The TLI method uses an infiltrant material similar in composition to the skeleton, but also containing a melting-point depressant (MPD), which allows the liquid metal to fill the skeleton void space and later facilitates homogenization. The materials requirements for such a system are discussed, and four experimental material systems were developed with final compositions of approximately Ni-40 wt pct Cu, Ni-4 wt pct Si, Fe-3 wt pct Si, and Fe-12 wt pct Cr-1 wt pct C, with copper, silicon, and carbon serving as the MPDs. Infiltration techniques include gating the introduction of liquid, saturating the melt to prevent erosion, and controlling variations in bulk composition along the infiltration path. Infiltration lengths exceeded 200 mm in the two nickel systems and exceeded 100 mm in the two iron systems. After infiltration, various heat treatments were conducted and mechanical properties were tested, including the tensile, hardness, and impact strength.
Similar content being viewed by others
References
Emanuel Sachs, Edward Wylonis, Samuel Allen, Michael Cima, and Honglin Guo: Polymer Eng. Sci., 2000, vol. 40 (5), pp. 1232–47.
Adam Lorenz, Emanuel Sachs, and Samuel Allen: Metall. Mater. Trans. A, 2004, vol. 35A, pp. 641–53.
K.A. Thorsen, S. Hansen, and O. Kjaergaard: Powder Metall. Int., 1983, vol. 15 (2), pp. 91–93.
S. Banerjee, R. Oberacker, and C.G. Goetzel: in Modern Developments in Powder Metallurgy, Metal Powder Industries Federation, Princeton, NJ, 1984, vol. 16, pp. 209–44.
Robert P. Messner and Yet-Ming Chiang: J. Am. Ceram. Soc., 1990, vol. 73 (5), pp. 1193–1200.
Leszek Hozer and Yet-Ming Chiang: J. Mater. Res., 1996, vol. 11 (9), pp. 2346–57.
F. Lenel, R. German, R. Heckel, and P. Mirchandani: in ASM Handbook, vol. 7, Powder Metallurgy, ASM, Metals Park, OH, 1984, pp. 308–21.
Randall German: Powder Metallurgy Science, 2nd ed., Metal Powder Industries Federation, Princeton, NJ, 1994.
S.F. Corbin: Metall. Mater. Trans. A, 2002, vol. 33A, pp. 117–24.
Akan Oton: Master’s Thesis, MIT, Cambridge, MA, June 1998.
W.D. MacDonald and T.W. Eagar: Metall. Mater. Trans. A, 1998, vol. 29A, pp. 315–25.
Alloy Phase Diagrams, vol. 3, ASM Handbook, ASM, Metals Park, OH, 1992, pp. 2–318, 2–173, 2–110, and 2–203.
Smithells Metals Reference Book, 7th ed., E.A. Brandes and G.B. Brook, eds., Butterworth Heinemann, Oxford, United Kingdom, 1992.
Adam Lorenz: Ph.D. Thesis, MIT, Cambridge, MA, 2002.
Thermo-Calc Software, a Computational Thermodynamics program developed at the Royal Institute of Technology, KTH, Stockholm, using the Kaufman Binary Database.
Vinay Prabhakar: Master’s Thesis, MIT, Cambridge, MA, 2002.
George W. Scherer: J. Non-Crystalline Solids, 1987, vol. 92, pp. 375–82.
Adrian E. Scheidegger: The Physics of Flow through Porous Media, 3rd ed., University of Toronto Press, Toronto, Canada, 1974.
K. Ishizaki, S. Komarneni, and M. Nanko: Porous Materials, Process Technology and Applications, Kluwer Academic Publishers, Boston, MA, 1998, pp. 202–23.
Annual Book of ASTM Standards, Designation E 8–96a, ASTM, Philadelphia, PA, 1997.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lorenz, A., Sachs, E., Kernan, B. et al. Densification of a powder-metal skeleton by transient liquid-phase infiltration. Metall Mater Trans A 35, 631–640 (2004). https://doi.org/10.1007/s11661-004-0375-2
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-004-0375-2