In this letter, we demonstrated the growth of different morphologies of silver submicrostructures influenced by o-phenylenediamine (oPD) concentrations and pH values. The results indicated that concentration ratios of the oPD to Ag+ colloids in the solution determine the final morphology of the products. oPD is found to act as a stabilizer as well as reduction agent. Particle shape ranges from sheets to spheres, increasing with molar ratio. Meanwhile, morphologies of structures and the time consumption to form particles both depend on pH values. We could obtain plates, polyhedrons, spheres, and dendrites through adjusting pH from 1.3 to 12.3. A mechanism is proposed to interpret the controlled synthesis of silver submicrostructures.
Similar content being viewed by others
References
Pradeep T, Anshup (2009) Thin Solid Films 517:6441
De D, Pal A, Jana NR, Pal TJ (2000) Photochem Photobiol A Chem 131:111
El-Sayed MA (2001) Acc Chem Res 34:257
Suber L, Sondi I, Matijevic E, Goia DV (2005) J Colloid Interface Sci 288:1489
Nikoobakht B, El-Sayed MA (2003) Chem Mater 15:1957
Huang CC, Yang Z, Chang HT (2004) Langmuir 20:6089
Huang Y, Lin Y, Chang H (2006) Nanotechnology 17:4885
Yang S (2007) Colloids and Surfaces A Physicochem Eng Aspects 301:174–183
Khan Z, Talib A (2010) Colloids Surf, B 76:164–169
Lee PC, Miesel DJ (1982) J Phys Chem 86:3391
Creigton J, Blatchford C, Albercht M (1979) J Chem Soc Faraday Trans 75:790
Xiong Y, Washio I, Chen J, Cai H, Li Z, Xia Y (2006) Langmuir 22:8563
Wei GD, Deng Y, Nan CW (2003) Chem Phys Lett 367:512
Wei GD, Nan CW, Deng Y, Lin YH (2003) Chem Mater 15:4436
Sun X, Dong S, Wang E (2005) J Colloid Interface Sci 290:130
Esumi K, Suzuki A, Aihara N, Usui K, Torigoe K (1998) Langmuir 14:3157
Dahl JA, Maddux BLS, Hutchison JE (2007) Chem Rev 107:2228
Sun X, Dong S, Wang E (2005) Langmuir 21:4710
Maye MM, Zheng W, Leibowitz FL, Ly NK, Zhong C-J (2000) Langmuir 16:490
Im SH, Lee YT, Wiley B, Xia Y (2005) Angew Chem Int Ed 44:2154
Siekkinen AR, McLellan JM, Chen J, Xia Y (2006) Chem Phys Lett 432:491
Lee YT, Im SH, Wiley B, Xia Y (2005) Chem Phys Lett 411:479
Premasiri AH, Euler WB (1995) Macromol Chem Phys 196:3655–3666
Hao Q, Sun B, Yang X, Lu L, Wang X (2009) Mater Lett 63:334–336
Turkevich J, Stevenson PC, Hillier J (1951) Discuss Faraday Soc 11:55
Marks LD (1994) Rep Prog Phys 57:603
Nam HS, Hwang NM, Yu BD, Yoon JK (2002) Phys Rev Lett 89:275502
Kan CX, Zhu XG, Wang GH (2006) J Phys Chem B 110:4651
Sun X, Hagner M (2007) Langmuir 23:10441
Zhang L, Chai L, Zhihui Yang H (2010) Materials Letters 64:1193–1196
Turkevich J (1985) Gold Bull 18:125
Blinova NV, Stejskal J, Trchova M (2009) Polymer 50:50–56
Sun X, Dong S, Wang E (2005) J Am Chem Soc 127:13102
Li XG et al (2005) Chem Mater 17:5411–5419
Li XG et al (2009) Langmuir 25:1675–1684
Huang MR, Peng QY, Li XG (2006) Chem Eur J 12:4341
Ershov BG, Janata E, Henglein A (1993) J Phys Chem 974:589
Janata E, Henglein A, Ershov BG (1994) J Phys Chem 98:10888
Linnert T, Mulavaney P, Henglein A (1993) J Phys Chem 97:679
Daniel MC, Astruc D (2004) Chem Rev 104:293
J. Sharma, R. Chhabra, H. Yan, Y. Liu (2007) Chem. Commun 477.
Liu Z, Zu Y, Fu Y, Guo S, Zhang Y, Liang H (2008) J Nanopart Res 10:1271
Acknowledgment
The work was supported by China West Normal University Innovation Fund.
Author information
Authors and Affiliations
Corresponding author
Additional information
An erratum to this article can be found at http://dx.doi.org/10.1007/s11581-011-0548-0
Rights and permissions
About this article
Cite this article
Fang, L., Zhou-feng, W. & Xing-Qi, H. Growth of different morphologies of silver submicrostructures: The effect of concentrations and pH. Ionics 17, 177–182 (2011). https://doi.org/10.1007/s11581-010-0499-x
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11581-010-0499-x