Compressive behaviour of Kevlar 49 fibres and composites

  • Papers
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

The low compressive strength of Kevlar 49® unidirectional composites cannot be satisfactorily explained in terms of current theories which assume that failure is due to the matrix material. For a given matrix, Kevlar 49 composites are considerably weaker in compression than those based on other comparable high strength, high modulus filaments. Fracture is found to occur before any plastic deformation of the matrix is observed.

This behaviour can be explained in terms of the very low compressive yield strength of the Kevlar 49 fibres themselves. Elastica loop tests show that non-Hookean deformation of the fibres occurs at quite low stresses corresponding to values of the order of those at which fracture takes place in the composite. This deformation is plastic in nature.

Buckled areas on the compression side of the elastica loop can be seen in the optical and scanning electron microscopes. It is suggested that the buckling follows from the separation of microfibrils under compression.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. G. B. Carter and V. T. J. Schenk, Physics Bulletin 24 (1973) 716.

    Google Scholar 

  2. J. W. Moore and D. L. G. Sturgeon, Composites 4 (1973) 34.

    Google Scholar 

  3. W. Däppen, Kunststoffe 63 (1973) 919.

    Google Scholar 

  4. J. R. Lager and R. R. June, J. Composite Materials 2 (1968) 178.

    Google Scholar 

  5. B. W. Rosen, “Mechanics of Composite Strengthening” in “Fibre Composite Materials” (American Society for Metals, Metals Park, Ohio, 1965) p. 37.

    Google Scholar 

  6. H. Kossira, Dissertation, Technische Hochschule, Stuttgart, 1963.

    Google Scholar 

  7. T. Hayashi, 7th International Reinforced Plastics Conference, Brighton, 20–22 October, 1970, Paper 11. British Plastics Federation, London.

    Google Scholar 

  8. D. Sinclair, J. Appl. Phys. 21 (1950) 380.

    Google Scholar 

  9. W. R. Jones and J. W. Johnson, Carbon 9 (1971) 645.

    Google Scholar 

  10. W. S. Williams, D. A. Steffens and R. Bacon, J. Appl. Phys. 41 (1971) 4893.

    Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Rights and permissions

Reprints and permissions

About this article

Cite this article

Greenwood, J.H., Rose, P.G. Compressive behaviour of Kevlar 49 fibres and composites. J Mater Sci 9, 1809–1814 (1974). https://doi.org/10.1007/BF00541750

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF00541750

Keywords

Navigation